KTA Crystal

Ọdịdị kristal:Orthorhombic, Point Group mm2

Parameter Lattice:a=13.125Å, b=6.5716Å, c=10.786Å

Ebe mgbaze:1130 ˚C

1130 ˚C:nso 5

Njupụta:3.454g / cm3

Nrụpụta okpomọkụ:K1:1.8W/m/K;K2: 1.9W/m/K;K3: 2.1W/m/K

WhatsApp Zitere anyị email Budata dị ka PDF

Nkọwa ngwaahịa

Usoro nka

Vidiyo

Potassium Titanyle Arsenate (KTiOAsO4), ma ọ bụ KTA kristal, bụ ọmarịcha kristal anya na-adịghị anya maka ngwa ngwa Parametric Oscillation (OPO).Ọ nwere ọnụọgụ ngwa anya na-abụghị nke ahịrị na nke eletrọnịkị, belata nnabata nke ukwuu na mpaghara 2.0-5.0 µm, bandwit sara mbara na ọnọdụ okpomọkụ, obere ala dielectric.Na omume ionic dị ala ya na-ebute oke mmebi dị elu ma e jiri ya tụnyere KTP.
A na-ejikarị KTA eme ihe dị ka ihe nrịbama OPO / OPA maka mgbapụta na oke 3µm yana kristal OPO maka ikuku na-echekwa anya na ike dị elu.
Njirimara:
Na-atụgharị n'etiti 0.5µm na 3.5µm
Ịrụ ọrụ ngwa anya na-abụghị nke kwụ ọtọ
Nnukwu nnabata okpomọkụ
Obere birefringence karịa KTP na-ebute nkwụsịtụ dị nta
Ọkachamara ngwa anya na enweghị linear homogeneity
Ọnụ ụzọ mmebi dị elu nke mkpuchi mkpuchi AR:> 10J/cm² na 1064nm maka pulses 10ns
Mkpuchi AR nwere obere nnabata na 3µm dị
Tozuru oke maka ọrụ oghere

Njirimara ndị bụ isi
Ọdịdị kristal	Orthorhombic, Point Group mm2
Lattice Parameter	a=13.125Å, b=6.5716Å, c=10.786Å
Ebe Na-agbaze	1130 ˚C
Mohs ike	nso 5
Njupụta	3.454g / cm3
Nrụpụta okpomọkụ	K1:1.8W/m/K;K2: 1.9W/m/K;K3: 2.1W/m/K

Njirimara ngwa anya na adịghị adị
Oke nghọta	350-5300nm
Ọnụọgụ absorption	@ 1064 nm <0.05%/cm
	@ 1533 nm <0.05%/cm
	@ 3475 nm <5%/cm
Nsogbu NLO (pm/V)	d31 = 2.76, d32 = 4.74, d33 = 18.5 , d15 = 2.3, d24 = 3.2
Electro-optical constants (pm/V)(obere ugboro)	ｒ33=37.5;ｒ23=15.4;ｒ13=11.5
Usoro SHG nwere ike kwekọrịtara	1083-3789nm