Kristal AgGaS2


  • Nsogbu Wavefront: erughị λ / 6 @ 633 nm
  • Dimension ndidi: (W +/- 0.1 mm) x (H +/- 0.1 mm) x (L +0.2 mm / -0.1 mm)
  • Clear oghere: > 90% etiti mpaghara 
  • Ewepụghị: λ / 6 @ 633 nm maka T> = 1.0mm
  • Elu elu: Achacha / gwuru 20/10 kwa MIL-O-13830A 
  • Ndekota: mma karịa 1 aak min
  • Nkwado: 5 aak nkeji
  • N'akuku ndidi: Δθ <+/- 0.25o, Δφ <+/- 0.25o
  • Product Ihe

    Nka na ụzụ

    Akụkọ ule

    Vidio

    AGS gosipụtara site na 0.50 ruo 13.2 µm. Ọ bụ ezie na ọnụọgụ ọnụọgụ ya na-enweghị atụ bụ nke kachasị dị ala n'etiti kristal ndị a kpọtụrụ aha infrared, a na-eji usoro ntụgharị ọhụụ dị mkpirikpi dị elu na 550 nm mee ihe na OPOs nke Nd: YAG laser; na ọtụtụ dị iche iche ugboro agwakọta nwere na diode, Ti: Sapphire, Nd: YAG na Iye dai lasers ekpuchi 3-12 µm nso; na usoro mgbochi infrared kpọmkwem, yana maka SHG nke CO2 laser. Thin AgGaS2 (AGS) efere kristal na-ewu ewu maka ọgbọ ultrashort pulse n'etiti etiti IR site na ọgbọ dị iche iche na-eji ọrụ ntụgharị NIR.
    Ngwa:
    • Ọgbọ nke abụọ nke ọgbọ na CO na CO2 - lasers
    • Ngwa anya parametric oscilator
    • Dị iche iche ugboro generator na etiti infrared mpaghara ruo 12 mkm.
    • Ugboro ugboro agwakọta n'etiti mpaghara IR site na 4.0 ruo 18.3 µm
    • Tuneable siri ike ala lasers (OPO pumped site Nd: YAG na ndị ọzọ lasers-arụ ọrụ na 1200 ka 10000 nm mpaghara na arụmọrụ 0.1 ka 10%)
    • Optical warara-gbalaga nzacha na mpaghara nso isotropic ebe (0.4974 m na 300 Celsius K), nnyefe gbalaga na-ekiri na okpomọkụ mgbanwe
    • Mgbanwe nke CO2 laser radieshon oyiyi n'ime nso-IR ma ọ bụ mpaghara a na-ahụ anya site na iji / ma ọ bụ iji Nd: YAG, rubi ma ọ bụ dye lasers na arụmọrụ ruo 30%

    Akụkụ:

    Standard cross ngalaba bụ 8x 8mm, 5 x 5mm, Crystal ogologo nso si 1 30 mm. Omenala nha bụkwa ndị dị na arịrịọ.

     

    Njirimara Ebumnuche
    Ngwunye ọkụ a = 5.757, c = 10.311 Å
    Ngwunye na-enweghị usoro na 10.6 um d36 = 12.5 elekere / V
    Mbibi ngwa anya dị na 10.6 um, 150 ns 10 - 20 MW / cm2
    ukem na c-axis 12.5 x 10-6 x ° C-1
    perpendicular ka c-axis -13,2 x 10-6 x ° C-1
    Nhazi kristal Tetragonal
    Mkpụrụ sel a = 5,756 Å, c = 10,301 Å
    Ebe mgbaze 997 Celsius
    Njupụta 4.702 g / cm3
    Mohs ekweghị ekwe 3-3.5
    Nnukwu nnabata 0,6 cm-1 @ 10,6 µm
    Ikwu Dielectric Constant @ 25 MHz s11s = 10 ε11t = 14
    Kwes Mgbasawanye ọnụọgụ || C: -13.2 x 10-6 /oC ⊥C: + 12.5 x 10-6 /oC
    Omume Omume nke Igwe 1.5 W / M / ° C
    Njirimara Ngwa Nweta Linear
    Uzo doro anya 0.50-13.2 um
    Ntụgharị Refract @ 1.064 um @ 5.300 um @ 10.60um ọ dịghị 2.4521 2.3945 2.3472 ne 2.3990 2.3408 2.2934
    Thermo-Optic ọnụọgụ dno / dt = 15,4 x 10-5 / ° C dne / dt = 15,5 x 10-5 / ° C
    Sellmeier akụkụ (ʎ na um) no2 = 3.3970 + 2.3982 / (1-0.09311 / ʎ2) + 2.1640 / (1-950 / ʎ2) ne2 = 3.5873 + 1.9533 / (1-0.11066 / ʎ2) + 2.3391 / (1-1030.7 / ʎ2)
    Njirimara Anya Njirimara
    Na-adọ-kenha SHG iche 1.8-11.2 um
    NLO Nwadota @ 1.064 um d36 = d24 = d15 = 23.6 mgbede / V
    Linear Electro-optic Coefficients Y41T = 4.0 pm / V Y63T = 3.0 elekere / V
    Mbibi ụzọ @ ~ 10 ns, 1.064 um 25 MW / cm2 (elu), 500 MW / cm2 (nnukwu)
    Nka na ụzụ
    Mgbaghara Wavefront erughị λ / 6 @ 633 nm
    Dimension ndidi (W +/- 0.1 mm) x (H +/- 0.1 mm) x (L +0.2 mm / -0.1 mm)
    Clear oghere > 90% etiti mpaghara
    Ewepụghị λ / 6 @ 633 nm maka T> = 1.0mm
    Elu Elu Achacha / gwuru 20/10 kwa MIL-O-13830A
    Ndekota mma karịa 1 aak min
    Ndabere 5 aak nkeji
    Nkịtị ndidi Δθ <+/- 0.25o, Δφ <+/- 0.25o

    AGS (AgGaS2) kristal Nzipu Spectra (Mgbe o siri ike polishing)
    Ule ule = 20.8mm (Ọkpụkpụ ikpeazụ = 20mm)
    Ntughari ụdịdị nke ụdị AgGaS2 a na-ekpuchi ekpuchi. OPO gbara site na 1030nm laser.ZnGeP201 AgGaS2 (AGS) kristal gosipụtara ezigbo mma dị ukwuu n'ofe nnyefe ahụ, na-atụ anya maka ihe mmịpụta ray nke dị n'akụkụ 1.8um. Njirimara nke AGS na-ekwe ka mmekọrịta SFM / DFM dị iche iche site na nke a na-ahụ anya na Middle infrared. ZnGeP201

    AGS (AgGaS2) kristal Nzipu spectra (Uncoated) Ule ọkpụrụkpụ = 1.60mm: ZnGeP201